PR2032 |
PH3660 |
Test Method |
顏色 Color |
淺琥珀色 |
琥珀色 |
Visual |
黏度 Viscosity 77℉ |
1650 cps |
150-175 cps |
ASTM D2392 |
比重 Specific Gravity |
1.15 |
0.96 |
ASTM D1475 |
重量混合比 |
- |
100 : 27 |
PTM&W |
操作時間 |
- |
30 min |
ASTM D2471 |
|
PR2032 搭配 PH3660硬化劑 |
Test Method |
|||
| 無加強材 | 玻璃纖維 | 碳纖維 | 克維拉纖維 | ||
混合比 Mix Ratio |
100 : 27 或 體積 3:1 |
PTM&W |
|||
操作時間 |
60 min |
ASTM D2471 |
|||
顏色 Color |
淺琥珀色 |
Visual |
|||
混合黏度 Mixed Viscosity @77℉ |
900-950 cps |
ASTM D2393 |
|||
硬化後硬度 Cured Hardness |
88 Shore D |
ASTM D2240 |
|||
比重 Specific Gravity, grams, cc |
1.11 |
ASTM D1475 |
|||
密度 Density |
0.0401 |
ASTM D792 |
|||
比容 Specific Volume, cu. in./lb. |
25.0 |
ASTM D792 |
|||
拉伸強度 Tensile Strength, psi |
9828 |
45,170 | 75,640 | 45,400 | ASTM D638 |
伸長率 Elongation at Break, % |
1.90% | 1.96% | 0.91% | 1.31% | ASTM D638 |
拉伸模數Tensile modulus, psi |
418,525 |
2,620,000 | 8,170,000 | 3,770,000 | ASTM D638 |
撓曲強度 Flexural Strength, psi |
16,827 |
62,285 | 96,541 | 34,524 | ASTM D790 |
撓曲模數 Flexural Modulus, psi |
462,910 | 2,560,000 | 6,480,000 | 2,500,000 | ASTM D790 |
玻璃轉換溫度 |
196℉ |
TMA |
|||
熱膨脹係數 |
4.3 x 10-5 |
ASTM D696 |
|||
測試材料: (1)玻璃纖維 #181 十層 (2)碳纖維 5.6 oz. 3K Fabric 十層 (3)克維拉纖維 5.0 oz. 十層 |
|||||